Construction Hardware - Wire Mesh Tie Wire, Galvanized Wire - Petron Pacific.Inc Global Steel and Wire source

Wire

High Tensile

Petron Pacific offers high tensile wire for the industries where high tensile strength is needed. High tensile wire is galvanized and used for security usage or together used with vineyard for plant support.

Materials: Carbon steel.
Wire Diameter: 2mm to 4 mm
Forms of Supply: In coils.

P C Strand are widely used in the construction of bridges, car parking garages, nuclear reactors, slabs, silos, hangars, aquaducts, high rise buildings, viaducts & railway sleepers .
It is manufactured as per any other International Specifications and as per customer requirements. They are available in many sizes such as plain, indented & galvanized form.

Vineyard

Class I - Standard
Class III - Special order
Galvanized extra high Tensile
Manufactured to ASTM - A641 specification
Min. PSI 170K lbs, Max. PSI 220k lbs
1,000 lb continuous Class I or Class III stands available on request

Aluminum - Clad Steel Reinforced (ACSR)

ACSR Core wire is used in reinforcement of aluminium conductors used in distribution and transmission of electricity. Qualities are close combination of high strength and ductility, Consistency of physical properties, Uniform and appropriate surface finish, Proper coil characteristic and uniform winding.

International Standard

ASTM B498 - 93 Class A Coating

ASTM Standard

Nominal Diameter mm		Size Tolerance mm		Ultimate Tensile Strength Min>		Stress at 1 % Extension Min>		% Elongation Min	Zn coating Min	Wrapping Mandrel Dia
From	To - Incl.	+	-	MPa	Kg/mm2	MPa	Kg/mm2	GL = 250 mm	g/m2	mm
1.270	1.521	0.038	0.025	1450	148	1310	133	3	183	3d
1.524	1.902	0.038	0.025	1450	148	1310	133	3	198	3d
1.905	2.283	0.038	0.025	1450	148	1310	133	3	214	3d
2.286	2.639	0.051	0.051	1410	144	1280	130	3.5	229	4d
2.642	3.045	0.051	0.051	1410	144	1280	130	3.5	244	4d
3.048	3.553	0.076	0.051	1410	144	1240	126	4	259	4d
3.556	4.569	0.102	0.076	1380	141	1170	119	4	274	5d
4.572	4.822	0.102	0.076	1380	141	1170	119	4	305	5d

BS EN 50189 : 2000 - ST 1A Grade-Mechanical Properties>

British Standard

Nominal Diameter mm		Size Tolerance mm	Ultimate Tensile Strength min		Stress at 1 % Extension min		% Elongation min	No. of torsion min	Wrapping Mandrel Dia
From	To - Incl.	+/-	N/mm²	Kg/mm²	N/mm²	Kg/mm²	GL = 250 mm	GL=100xd	mm
1.24	1.5	0.03	1400	143	1170	119	3	18	1d
1.50	1.75	0.03	1400	143	1170	119	3	18	1d
1.75	2.25	0.03	1400	143	1170	119	3	18	1d
2.25	2.75	0.04	1350	137	1140	116	3	16	1d
2.75	3.00	0.05	1350	137	1140	116	3.5	16	1d
3.00	3.5	0.05	1300	132	1100	112	3.5	14	1d
3.50	4.25	0.06	1300	132	1100	112	4	12	1d
4.25	4.75	0.06	1300	132	1100	112	4	12	1d
4.75	5.5	0.07	1300	132	1100	112	4	12	1d

ASTM B498 - 93 Class A Coating

ASTM Standard

Nominal Diameter mm		Size Tolerance mm		Ultimate Tensile Strength Min		Stress at 1 % Extension Min		% Elongation Min	Zn coating Min	Wrapping Mandrel Dia
From	To - Incl.	+	-	MPa	Kg/mm2	MPa	Kg/mm2	GL = 250 mm	g/m2	mm
1.270	1.521	0.038	0.025	1450	148	1310	133	3	183	3d
1.524	1.902	0.038	0.025	1450	148	1310	133	3	198	3d
1.905	2.283	0.038	0.025	1450	148	1310	133	3	214	3d
2.286	2.639	0.051	0.051	1410	144	1280	130	3.5	229	4d
2.642	3.045	0.051	0.051	1410	144	1280	130	3.5	244	4d
3.048	3.553	0.076	0.051	1410	144	1240	126	4	259	4d
3.556	4.569	0.102	0.076	1380	141	1170	119	4	274	5d
4.572	4.822	0.102	0.076	1380	141	1170	119	4	305	5d

BS EN 50189 : 2000 - ST 1A Grade-Mechanical Properties

British Standard

Nominal Diameter mm		Size Tolerance mm	Ultimate Tensile Strength min		Stress at 1 % Extension min		%Elongation min	No. of torsion min	Wrapping Mandrel Dia
From	To - Incl.	+/-	N/mm²	Kg/mm²	N/mm²	Kg/mm²	GL = 250 mm	GL=100xd	mm
1.24	1.5	0.03	1400	143	1170	119	3	18	1d
1.50	1.75	0.03	1400	143	1170	119	3	18	1d
1.75	2.25	0.03	1400	143	1170	119	3	18	1d
2.25	2.75	0.04	1350	137	1140	116	3	16	1d
2.75	3.00	0.05	1350	137	1140	116	3.5	16	1d
3.00	3.5	0.05	1300	132	1100	112	3.5	14	1d
3.50	4.25	0.06	1300	132	1100	112	4	12	1d
4.25	4.75	0.06	1300	132	1100	112	4	12	1d
4.75	5.5	0.07	1300	132	1100	112	4	12	1d